Phenolic cotton rods

Characteristics: Winded and pressed bars of hardened fabric are made of cotton fabric and phenolic resin.

Applications: They are suitable for the manufacture of various mechanically and electrically loaded components, plain bearings, housings, small-gear gears.

Production dimensions: Textile rods are made from 6 mm in diameter to 200 mm in diameter. Production lengths of rods: 1000 mm.

Type according EN-60893 Unit PFCC42
Used name Phenolic cotton rod
Type according to DIN 7735 Hgw2088
Type according to NEMA  
Reinforcement cotton fabric
Resin phenol
     
MECHANICAL PROPERTIES    
Flexural strength flatwise perpendicular to laminations (at 20°C) MPa 110
Compressive strength perpendicular to laminations MPa 185
     
DIELETRIC PROPERTIES    
Dielectric strength perpendicular to layers in oil 90°C kV 5
Insulation resistance after immersion in water MΩ 40
     
PHYSICAL PROPERTIES    
Density g/cm3 1,2 - 1,4
Temperature index (TI)   120
Water absorption (for thickness 3 mm) mg/cm3 3
Flammability (category)  

Note: The above values in the table are informative only. Technical sheets for individual products on request.

News
13.10. 2022

PLASTEX 2022

At the beginning of October 2022, we exhibited at the PLASTEX international fair, dedicated to plastics, rubber and composite comodities. Plastex was held as a part of the…
17.6. 2022

CWIEME 2022

At the beginning of May, we exhibited at the CWIEME trade fair in Germany. We met with our customers and suppliers. After a long covid break, these meetings were very nice. …
Contact
LABARA s.r.o.
Jindřichov 33
595 01 Velká Bíteš
tel.: +420 566 533 128
fax: +420 566 533 111
e-mail: This email address is being protected from spambots. You need JavaScript enabled to view it.
Nahoru